Total Weight | 185 gsm ± 20gsm |
Total Weight of Carbon | 100gsm ± 20gsm |
Thickness | 1.0 ± 0.2 mm |
Air Permeability | above 250litres/m2/sec at 200Pa |
Tear strength | >20N |
Delamination strength | >3N |
Delamination strength after washing (6 cycles) | >3N |
Tensile strength | >50N |
Loss of carbon after washing (6 cycles) | <3% of construct |
Performance vs mustard gas | >10 hours |
Performance vs mustard gas after exposure to petrol | >10 hours |
Performance vs mustard gas after exposure to saline solution |
>10 hours |
Performance vs mustard gas after exposure to Washing (6 cycles) |
>10 hours |
Performance vs mustard gas after artificial ageing (100°C and -15°C) |
>10 hours (100°C ageing) >10 hours (-15°C ageing) |